18Ni Maraging Steel化學(xué)成分 - AMS 6514

C	Si	Mn	P	S	Cr	Ni	Mo	Cu	Co	Al	Ti	Fe
≤0.03	≤0.10	≤0.10	≤0.010	≤0.010	≤0.50	18.00-19.00	4.60-5.20	≤0.50	8.50-9.50	0.05-0.15	0.50-0.80	≤Bal

---

18Ni Maraging Steel標(biāo)準(zhǔn)規(guī)范

• AMS 6514 -
• ASTM A 538 -
• Mil-S-46850D -
• UNS K93120 -

---

18Ni Maraging Steel機械性能

MARAGING (C) 300
General: Maraging is a 18% nickel, cobalt strengthened steel (C-type), with excellent mechanical properties, workability and heat
treatment characteristics.
Applications: Typical applications for maraging include missile and rocket motor cases, landing and takeoff gear, munitions,
aerospace, extrusion tooling, die casting, high performance shafting, gears and fasteners.
Composition:
C Mn Si P S NI
0.03 max 0.10 max 0.10 max 0.010 max 0.010 max 18.00-19.00
Co Mo Ti Al Cr Cu
8.50-9.50 4.60-5.20 0.50 -0.80 0.05-0.15 0.50 max 0.50 max Fe Bal
Material Melt Method: Maraging melt method is a VIM (Vacuum Induction Melt) + VAR (Vacuum Arc Remelt)
As Shipped Condition: Maraging is supplied in the annealed and descaled condition. The alloy is very tough, relatively soft (36
Rc Max.), therefore, readily machined and formed.
*Bar Tolerances: .250” - .499” .500” - .999” 1.000” – 3.625” 3.626” – 6.000” 6.001” – 8.000” 8.001” – 10.000”
-.000/+.005 -.000/+.010 -.000/+.031 -.000/+.047 -.000/+.063 -.000/+0.078
Minimum Properties after Aging:
Hardness ……………… 52 Rc Charpy V-notch ……… 12 ft/lbs. min Reduction of Area ……. 47%
Elongation ……………. 5.0% Yield Strength …………. 280 ksi Fracture Toughness ….. 60
Physical Properties:
Density………………………………… .289 lbs./cu. In
Average Coefficient of Thermal Expansion (70 – 900 F) ……………… 5.6 x 10 -6 in/in. F
Heat Treatment Aging Process: (Non Die Casting Applications)
Material is to be heat treated to 900 F +/- 10 holding at temperature for 6 hours then cooling at room air temperature. During the aging
treatment maraging shrinks uniformly and predictably on all dimensions .001 in/in
Heat Treatment Aging Process: (Die Casting Applications)
Following the rough machining of the die, anneal at 1500-1525 F for 1 hour per inch of thickness is recommended. After finish
machining , an aging heat treatment of 980-1000 F for 6 hours is recommended.
Machining:
Maraging steel in the annealed condition is comparable to 4340. However, when maraging is aged, the type of cutting tool and speeds
change. Rigid equipment, firm tool supports, sharp tools and abundant coolant are essential.
Welding:
Maraging is weld able without preheat, in both the annealed and aged condition. Only an aging heat treatment is needed to restore in the
weld.
Standards:
AMS 6514 ASTM A 538 *Mil-S-46850D UNS K93120
*DMI product is not supplied to the dimensional tolerances of MIL-S-46850D.
*The information, data and specifications presented here are representative only, and are not guaranteed values. Material or products
applications described are solely for illustrative purposes and should not be construed as express or implied warranties for fitness for these
or other applications

---

18Ni Maraging Steel產(chǎn)品形態(tài)

• 熱軋和冷拉棒材, 圓棒, 扁鋼, 六角棒, 八角棒, 空心棒
• 帶鋼和鋼卷, 熱軋帶鋼, 熱軋鋼卷, 冷軋鋼帶, 冷軋鋼卷
• 冷軋板材, 熱軋板, 冷軋薄板, 中厚板, 高強鋼板
• 熱軋和冷拉異型鋼, 凹凸字鋼, 滑軌, 滑塊
• 熱軋和冷拉鋼絲, 扁絲, 盤條, 直條
• 自由鍛和模鍛, 扁鋼, 模塊, 環(huán), 桶, 餅, 階梯軸及定制化
• 熱擠壓和冷軋無縫管, 異型管, 方管, 毛細管
• 電渣錠

---